dye sensitized solar cell was fabricated from a double layer photoanode. first, tio2 nanoparticles  were synthesized by hydrothermal method. these tio2 nps were deposited on fto glasses by electrophoretic deposition  method in applied voltage of 5 v and epd time of 2.5-10 min. then tio2 hollow spheres (hss) were synthesized by sacrificed template method with carbon spheres as template and ttip ...

While the synthesis of TiO2 hollow structures is well-established, in most cases it is particularly difficult to control the crystallization of TiO2 in solution or by calcination. As a result, TiO2 hollow structures do not really exhibit enhanced lithium storage properties. Herein, we report a simple and cost-effective template-assisted method to synthesize anatase TiO2 hollow spheres composed ...

Solid amorphous TiO2 mesospheres were synthesized by controlled hydrolysis of Ti-containing precursors. Subsequently, solid TiO2 mesospheres were exploited as scaffolds and subjected to a one-step external template-free hydrothermal treatment, yielding intriguing hollow anatase TiO2 mesospheres. The synthetic protocol was optimized by investigating the effect of buffer reagents and fluoride ion...

Titanium oxide hollow microspheres were synthesized from organic precursor titanium tetraisopropoxide (TTIP) using continuous spray pyrolysis reactor. Effects of precursor concentration, applied voltage and annealing have been investigated. It was observed that the annealing of the as-synthesized TiO2 hollow microspheres at 250C, which had an average external diameter of 200 nm, leads to an inc...

The nanostructures of TiO2 significantly affect its photocatalytic activity. In this work, various TiO2 nanostructures have been successfully synthesized, including one-dimensional (1D) TiO2 nanotube, 1D TiO2 nanowire, three-dimensional (3D) TiO2 sphere assembled by nanoparticles (TiO2 sphere-P) and 3D TiO2 sphere assembled by nanosheets (TiO2 sphere-S). The results of photodegradation activity...

In a mixed solvent of water and ethanol, polystyrene/titanium dioxide (PSt/TiO2) composite particles of core-shell structure were prepared by hydrolysis of tetrabutyl titanate in the presence of cationic PSt particles or anionic PSt particles surface-treated using γ-aminopropyl triethoxysilane. Hollow TiO2 particles were obtained through calcination of the PSt/TiO2 core-shell particles to burn ...

A general and facile one-pot template-free hydrothermal strategy has been developed to synthesize various metal oxide (TiO2, SnO2 and α-Fe2O3) hollow spheres with unified morphologies. The formation of hollow structure involves a trifluoroacetic acid (TFA)-assisted Ostwald ripening process. Photocatalytic activities of the as-prepared TiO2 product are evaluated by the photodegradation of Rhodam...

Nb, F-codoped TiO2 hollow spheres (NFTSs) were successfully synthesized via a hydrothermal method with niobium oxide, hydrofluoric acid, and tetrabutyl titanate. The obtained spheres were hollow, with a diameter of about 2 μm, and the sphere wall was made up of nanorods arranged close together. The NFTSs presented anatase phase with more {001} facets exposed, which could be mainly attributed to...

Currently, Degussa P25, with the typical mixed phases of anatase and rutile TiO2, is widely applied as the commercial photocatalysts. However, there are still some of obstacles for the P25 nanoparticles with totally high photocatalytic activities, especially for the catalytic stability due to their inevitable aggregation of the nanoparticles when used as the photocatalysts. In the present work,...

The development of high-efficiency photocatalysts plays an important role in the application solar energy conversion. Titanium dioxide (TiO2) with anatase crystalline phase is well-known as semiconductor thin layers for cells. This work has constructed a novel TiO2 hollow sphere (HST) 2-step synthesis. first step coating SiO2 template to build core-shell SiO2@TiO2 (CSST). second etching via son...